Temperature dependence of activation volume on Cu content of ultra-low carbon steel

Masaki Tanaka, Daichi Izumi, Nobuyuki Yoshimura, Genichi Shigesato, Manabu Hoshino, Kohsaku Ushioda, Kenji Higashida

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

The temperature dependence of the yield stress, effective stress and activation volume on the Cu content in steel was assessed using polycrystalline ultra-low carbon steels with 0.5, 1 and 2 mass% Cu added. A small hump was seen in the effective stress–temperature curve for ultra-low carbon steel, which has also been reported for high-purity single-crystal iron. The effective stress was found to decrease with increasing the Cu content. The activation volume was found to be linearly related to the temperature at low temperatures for all types of specimens considered. The activation volume was found to increase abruptly at a certain temperature, which increased with increasing the Cu content. The change in the relationship of the activation volume to temperature is discussed in this paper with respect to the thermally activated process of dislocation glide from the Peierls mechanism to the interaction between dislocations and solute Cu atoms.

本文言語英語
ページ(範囲)2915-2930
ページ数16
ジャーナルPhilosophical Magazine
97
31
DOI
出版ステータス出版済み - 8 16 2017

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics

フィンガープリント 「Temperature dependence of activation volume on Cu content of ultra-low carbon steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル