The effect of gangue composition on the behavior of the Fe3C synthesis

M. Egashira, T. Maeda, H. Nakagawa, M. Shimizu

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)


The purpose of this investigation is to clarify the effect of gangue composition (Al2O3, CaO, SiO2 and MgO) in the hematite pellets on the synthesis of Fe3C pellets. Pure hematite pellets and those contained one, two or three kinds of the gangue compositions were reacted in the atmosphere with H2-30vol%CH4 gas mixture at 750°C. It was confirmed that the Fe3C were produced when the pellets containing Al2O3 (1, 3, 5 mass%), MgO (1, 3, 5 mass%) and SiO2 (5 mass%) were reduced. All of the reduced pellets had the similar specific surface area. However, the structure of reduced iron phase were different form each other. The reduced pellets containing Fe3C had the iron phase with many micro pores, and the reduced pellets containing no Fe3C had that with no micro pores. For the pellets contained two or three kinds of the gangue compositions, it was recognized that the formation of Fe3C is suppressed by CaO and promoted by Al2O3.

ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
出版ステータス出版済み - 6 2001

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「The effect of gangue composition on the behavior of the Fe<sub>3</sub>C synthesis」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。