The effect of mean stress and hardness on the fatigue limit of material with small defect

Yoshiyuki Kondo, Chu Sakae, Masanobu Kubota, Takao Kudou

    研究成果: ジャーナルへの寄稿学術誌査読

    6 被引用数 (Scopus)

    抄録

    A small defect gives a substantial effect on the fatigue limit. The effects of mean stress and hardness on the fatigue limit of material with a small defect are quite different from those of a long crack nor a plain specimen. The following questions have been arisen. (1) Why does a harder material have a higher fatigue limit in case of material with a small defect? It is not a case in a long crack. (2) Is the mean stress effect on the fatigue limit of material with a small defect the same as that on the △Kth of a long crack? Fatigue tests were performed under a wide range of mean stress for two kinds of steels with different hardness using specimens with small defects. The crack closure of a short crack was measured. It was shown that the build up of the crack closure was affected by the material hardness and mean stress. This behavior of crack closure resulted in peculiar properties of fatigue limit in case of material with a small defect.

    本文言語英語
    ページ(範囲)1185-1191
    ページ数7
    ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
    68
    8
    DOI
    出版ステータス出版済み - 8月 2002

    !!!All Science Journal Classification (ASJC) codes

    • 材料科学(全般)
    • 材料力学
    • 機械工学

    フィンガープリント

    「The effect of mean stress and hardness on the fatigue limit of material with small defect」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル