The effect of simple heat treatment on apatite formation on grit-blasted/acid-etched dental Ti implants already in clinical use

Ayano Ogura, Seiji Yamaguchi, Phuc Thi Minh Le, Kayoko Yamamoto, Michi Omori, Kazuya Inoue, Nahoko Kato-Kogoe, Yoichiro Nakajima, Hiroyuki Nakano, Takaaki Ueno, Tomohiro Yamada, Yoshihide Mori

研究成果: Contribution to journalArticle査読

抄録

Grit-blasted/acid-etched titanium dental implants have a moderately roughened surface that is suitable for cell adhesion and exhibits faster osseointegration. However, the roughened surface does not always maintain stable fixation over a long period. In this study, a simple heat treatment at 600°C was performed on a commercially available dental Ti implant with grit-blasting/acid-etching, and its effect on mineralization capacity was assessed by examining apatite formation in a simulated body fluid (SBF). The as-purchased implant displayed a moderately roughened surface at the micrometer scale. Its surface was composed of titanium hydride accompanied by a small amount of alumina particles derived from the grit-blasting. Heat treatment transformed the titanium hydride into rutile without evidently changing the surface morphology. The immersion in SBF revealed that apatite formed on the heated implant at 7 days. Furthermore, apatite formed on the Ti rod surface within 1 day when the metal was subjected to acid and heat treatment without blasting. These indicate that apatite formation was conferred on the commercially available dental implant by simple heat treatment, although its induction period was slightly affected by alumina particles remaining on the implant surface. The heat-treated implant should achieve stronger and more stable bone bonding due to its apatite formation.

本文言語英語
ジャーナルJournal of Biomedical Materials Research - Part B Applied Biomaterials
DOI
出版ステータス受理済み/印刷中 - 2021

All Science Journal Classification (ASJC) codes

  • 生体材料
  • 生体医工学

フィンガープリント

「The effect of simple heat treatment on apatite formation on grit-blasted/acid-etched dental Ti implants already in clinical use」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル