The enhancement of the performance of dye sensitized solar cells using Nb 2O 5-TiO 2 compound

Seok Won Choi, Hyunwoong Seo, Min Kyu Son, Soo Kyoung Kim, Na Yeong Hong, Hee Je Kim, Jong Rak Kim

研究成果: ジャーナルへの寄稿学術誌査読

抄録

Niobium oxide (NbA) has a strong chemical coherence and good electrical conductivity. Therefore, this material is helpful to enhance the performance of the dye sensitized solar cells (DSC) by improving the electron mobility. In this study, Nb 2O 5 was mixed with TiO 2 and this compound was applied to the DSC to improve its performance. As a result, the current density of the DSC using the Nb 2O 5-TiO 2 compound on the photoelectrode was increased, because the internal resistance concerned to the electron transfer in the photoelectrode of DSC was decreased. However, large amount of the Nb 2O 5 induces the decrease of the efficiency of the DSC because the surface area to attach dye molecules is decreased due to the large particle of Nb 2O5. Therefore, it is important to optimize the mixture ratio of the Nb 2O 5-TiO 2 compound for maximizing the performance of the DSC. Finally, the most optimum performance of the DSC was shown in case of the Nb 2O 5 concentration of 10 wt% of the Nb 2O 5-TiO 2 compound.

本文言語英語
ページ(範囲)1153-1158
ページ数6
ジャーナルTransactions of the Korean Institute of Electrical Engineers
61
8
DOI
出版ステータス出版済み - 8月 2012

!!!All Science Journal Classification (ASJC) codes

  • 電子工学および電気工学

フィンガープリント

「The enhancement of the performance of dye sensitized solar cells using Nb 2O 5-TiO 2 compound」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル