The influence of static crack-opening stress on the threshold level for shear-mode fatigue crack growth in bearing steels

S. Okazaki, K. Wada, H. Matsunaga, M. Endo

研究成果: Contribution to journalArticle査読

16 被引用数 (Scopus)

抄録

An investigation was conducted into the influence of statically-applied, mode I, crack-opening load on the threshold condition for propagation of a shear-mode fatigue crack in a bearing steel. Torsional fatigue test was carried out at an R of −1 using a hollow cylindrical specimen into which a semi-elliptical, small slit was axially introduced. A static axial compressive stress was simultaneously applied to suppress crack branching. A coplanar, shear-mode, non-propagating fatigue crack emanating from the slit was attained by appropriate control of shear stress amplitude. Internal pressure was then applied to generate a hoop stress as a static crack-opening stress, σθ static. Consequently, the threshold shear-mode stress intensity factor range, ΔKτth, was significantly decreased with increase of the static mode I stress intensity factor. To further understand the contribution of σθ static to the reduction in ΔKτth, microstructural observations for the cross-sections of a non-propagating crack were conducted using a scanning electron microscope in conjunction with the electron backscatter diffraction analysis. The results revealed that the excess loading of σθ static accounts for the change in the crack-path, resulting in a further reduction in ΔKτth.

本文言語英語
ページ(範囲)127-138
ページ数12
ジャーナルEngineering Fracture Mechanics
174
DOI
出版ステータス出版済み - 4 1 2017

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「The influence of static crack-opening stress on the threshold level for shear-mode fatigue crack growth in bearing steels」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル