The preparation and property control of Zinc Oxide NPs

Yusuke Sakai, Chan Gi Lee, Masato Uehara, Hiroyuki Nakamura, Hideaki Maeda

研究成果: ジャーナルへの寄稿Conference article

抜粋

ZnO nanoparticles (NPs) have attracted increasing attention recently because it is nontoxic, chemically stable towards air, and inexpensive luminescent material instead of the GaN- based structures. However, in general, two emission peaks appear in the ultraviolet and visible region in the photoluminescence spectra of ZnO NPs because of trapping with surface states or a lattice defect. Therefore, in this study, we tried to control the defect of ZnO NPs to obtain pure band-edge emission peak, as well as to keep the dispersivity as colloidal solution. At first, we applied high temperature (300°C) to synthesize ZnO NPs, however, short reaction time (<30s) was not enough for obtaining pure-band-edge emission ZnO NPs, whereas long time (>120s) reaction made ZnO NPs to lose its colloidal stability and aggregated to decrease their PL intensity significantly. So, low synthesis temperature (200°C) was hardly obtaining emission peak even after 1h of heating. Therefore, it was tried to divide synthesis into two steps to generate ZnO NPs at high temperature (300°C) and to heal the defect with the dispersing quality keeping at low temperature (200°C). As a result, we succeed to suppress the defects of ZnO NPs and obtain the well-dispersed pure band-edge emission ZnO NPs.

元の言語英語
記事番号082026
ジャーナルIOP Conference Series: Materials Science and Engineering
18
発行部数SYMPOSIUM 5
DOI
出版物ステータス出版済み - 1 1 2011
イベント3rd International Congress on Ceramics, ICC 2011 - Osaka, 日本
継続期間: 11 14 201011 18 2010

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Engineering(all)

これを引用