The study on binary Mg-Co hydrogen storage alloys with BCC phase

Yao Zhang, Yoshinori Tsushio, Hirotoshi Enoki, Etsuo Akiba

研究成果: Contribution to journalArticle査読

63 被引用数 (Scopus)

抄録

Novel Mg-Co binary alloys were successfully synthesized by mechanical alloying. These alloys were studied by X-ray diffraction (XRD), transmission electron micrograph (TEM), pressure-composition-isotherms measurements (P-C-T) and differential scanning calorimetry (DSC). Both XRD Rietveld analysis and TEM observation confirmed that these binary alloys contain BCC phase and that the BCC phase existed in the range from 37 to 80 at.% Co. The lattice parameter of the BCC phase increased with the increase of the Co content from 37 to 50 at.%. When the Co content reached 50 at.%, the lattice parameter reached a maximum value, and then turned to decrease gradually with further increase of the Co content. Most of Mg-Co BCC alloys absorbed hydrogen at 373 K under 6 MPa of hydrogen pressure. The Mg60Co40 alloy showed the highest hydrogen absorption capacity, about 2.7 mass% hydrogen. However, all the Mg-Co alloys studied did not desorb hydrogen at 373 K. By means of DSC measurements and in situ XRD analysis, it was found that under 4 MPa hydrogen atmosphere, Mg50Co50 alloy transformed from BCC solid solution to Mg2CoH5 tetragonal hydride at 413 K.

本文言語英語
ページ(範囲)147-153
ページ数7
ジャーナルJournal of Alloys and Compounds
393
1-2
DOI
出版ステータス出版済み - 5 3 2005
外部発表はい

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「The study on binary Mg-Co hydrogen storage alloys with BCC phase」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル