Thermal analysis of structural phase transition behavior of Ln 2 Ni 1−x Cu x O 4+δ (Ln = Nd, Pr) under various oxygen partial pressures

Mamoru Sakai, Chengkun Wang, Takashi Okiba, Haruki Soga, Eiki Niwa, Takuya Hashimoto

研究成果: Contribution to journalArticle査読

9 被引用数 (Scopus)

抄録

Structural phase transition behavior between orthorhombic and tetragonal in Ln 2 Ni 1−x Cu x O 4+δ (Ln = Nd, Pr), which attracts interest as new cathode material for solid oxide fuel cells, has been investigated with thermal analysis under controlled oxygen partial pressures (P(O 2 )). For Nd 2 Ni 1−x Cu x O 4+δ with 0.0 ≤ x ≤ 0.1, temperature, enthalpy change (ΔH) and change in excess oxygen content (Δδ) at the phase transition decreased with increasing Cu content. The phase transition temperature decreased with decreasing P(O 2 ), whereas little variation was observed in ΔH and Δδ. For Nd 2 Ni 1−x Cu x O 4+δ with x ≥ 0.15, crystal structure was tetragonal and no phase transition was detected below 750 °C. For Pr 2 Ni 1−x Cu x O 4+δ with x = 0.0 and 0.1, phase transition was observed by DSC, showing similar dependence of phase transition temperature and ΔH on Cu content and P(O 2 ) with that of Nd 2 Ni 1−x Cu x O 4+δ . Δδ was not detected in TG curve of Pr 2 Ni 0.9 Cu 0.1 O 4+δ , which could be attributed to too small Δδ. From Ellingham diagram prepared using temperature and P(O 2 ) at the phase transition, variation of standard enthalpy (ΔH°) and standard entropy (ΔS°) was evaluated. It was revealed that variation of phase transition temperature by Cu content and difference of the phase transition temperature between Nd 2 Ni 1−x Cu x O 4+δ and Pr 2 Ni 1−x Cu x O 4+δ showed correspondence with variation of ΔH°. Excess oxygen content, δ, in Nd 2 Ni 1−x Cu x O 4+δ , evaluated with reduction in TG apparatus, decreased with increasing Cu content. It was suggested that some amount of δ was required for stabilization of orthorhombic phase and that low δ by Cu substitution stabilized the tetragonal structure of the specimens with x ≥ 0.15.

本文言語英語
ページ(範囲)2765-2774
ページ数10
ジャーナルJournal of Thermal Analysis and Calorimetry
135
5
DOI
出版ステータス出版済み - 3 15 2019
外部発表はい

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry

フィンガープリント 「Thermal analysis of structural phase transition behavior of Ln <sub>2</sub> Ni <sub>1−x</sub> Cu <sub>x</sub> O <sub>4+δ</sub> (Ln = Nd, Pr) under various oxygen partial pressures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル