Thermal molecular motion of polystyrene ultrathin films on various substrates

Keiichi Akabori, Keiji Tanaka, Toshihiko Nagamura, Atsushi Takahara, Tisato Kajiyama

研究成果: 会議への寄与タイプ学会誌査読

抄録

Thermal molecular motion of polystyrene (PS) ultrathin films on various substrates was examined by dynamic viscoelastic measurement. In the case of the ultrathin films on substrates, the αa-absorption peak corresponding to the segmental motion was broadened toward lower and higher temperature sides because of surface and interfacial effects. When a PS ultrathin film was sandwiched between SiOx layers, an interfacial αa-relaxation peak appeared at the higher temperature side in addition to the original peak from the internal phase. However, this was trivial for a PS ultrathin film between Al layers, instead, the original peak was shifted to the lower temperature side due probably to a chain confinement effect. Finally, it was concluded that the effects of free surface and a chain confinement activate the segmental motion, whereas interfacial interactions produce the opposite effect.

本文言語英語
ページ数1
出版ステータス出版済み - 12月 1 2005
イベント54th SPSJ Symposium on Macromolecules - Yamagata, 日本
継続期間: 9月 20 20059月 22 2005

その他

その他54th SPSJ Symposium on Macromolecules
国/地域日本
CityYamagata
Period9/20/059/22/05

!!!All Science Journal Classification (ASJC) codes

  • 工学(全般)

フィンガープリント

「Thermal molecular motion of polystyrene ultrathin films on various substrates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル