放電プラズマ焼結法により焼結・接合したAg層を有するFeSi<sub>2</sub>熱電変換モジュールの熱電変換特性

鈴木 裕宣, 藁谷 真也, 東 之弘, 髙澤 勇輝, 安野 拓也

研究成果: Contribution to journalArticle査読

抄録

To achieve high performance of thermoelectric conversion module, it is important that the contact electric resistance between thermoelectric element and electrode is decreased. The manufacturing method to perform sintering of FeSi<sub>2</sub> powder and joining of the sintered body with Ag metal plates at the same time was examined by using SPS(spark plasma sintering) method. The Ag plates were successfully joined to FeSi<sub>2</sub> element by this process. In addition, it was able to lower the resistance of thermoelectric conversion module because the contact electric resistance between the FeSi<sub>2</sub> element and the Cu electrode was decreased by joining Ag plates. The thermoelectric conversion modules with various element heights were produced by this process, and the performance of the modules was evaluated under several temperature differences. The most suitable thermoelectric module height, 5 mm, was decided by investigating relations of the module height and the performance. The FeSi<sub>2</sub> thermoelectric conversion module consisting of 50 pairs of p-n elements was produced using an element with 5 mm height, and the performance was measured. As a result, the maximum electric power of FeSi<sub>2</sub> thermoelectric conversion module of 50 pairs was 1.70 W in the condition of heating temperature at 873 K and/or cooling temperature at 293 K.
寄稿の翻訳タイトルThermoelectric Properties of FeSi<sub>2</sub> Thermoelectric Conversion Modules Sintered with Ag Joint Plates by Spark Plasma Sintering Method
本文言語日本語
ページ(範囲)313-317
ページ数5
ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
62
6
DOI
出版ステータス出版済み - 2015

フィンガープリント

「放電プラズマ焼結法により焼結・接合したAg層を有するFeSi<sub>2</sub>熱電変換モジュールの熱電変換特性」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル