Time and spatially resolved luminescence spectroscopy of ZnO nanostructures

Hideaki Murotani, Yoichi Yamada, Daisuke Nakamura, Tatsuo Okada

研究成果: 著書/レポートタイプへの貢献

抄録

The optical properties of undoped, P-doped, and Sb-doped ZnO nanostructures (NSs) have been studied by means of photoluminescence (PL), time-resolved PL, and spatially resolved cathodoluminescence (CL) spectroscopy. The temperature dependence of the PL spectra of the P-doped and Sb-doped ZnO NSs was analyzed, and the binding energies of the P-acceptor- and the Sb-acceptor-bound excitons were estimated to be 15 and 11 meV, respectively. This indicated that the Sb impurities formed a shallower acceptor level than the P impurities in ZnO. PL lines due to the radiative recombination of biexcitons and the inelastic scattering processes of excitons were clearly observed in the undoped ZnO NSs, which enabled us to evaluate the binding energies of the excitons and biexcitons as 60 and 15 meV, respectively. These values were identical to the values in bulk ZnO. The radiative and nonradiative recombination lifetimes were estimated from the temperature dependence of the PL lifetime and the time-integrated PL intensity. Although the radiative recombination lifetimes for the undoped and P-doped ZnO NSs were almost equal, the nonradiative recombination lifetime for the P-doped ZnO NSs was longer than that for the undoped ZnO NSs. This suggested that the P doping suppressed the thermal activation of the nonradiative recombination processes. CL images revealed that the intensity of the side surface was much stronger than that of the interior in the P-doped ZnO NSs. On the other hand, the CL intensity was distributed almost uniformly in the Sb-doped.

元の言語英語
ホスト出版物のタイトルZnO Nanocrystals and Allied Materials
編集者M.S. Ramachandra Rao, Tatsuo Okada
ページ195-216
ページ数22
DOI
出版物ステータス出版済み - 1 1 2014

出版物シリーズ

名前Springer Series in Materials Science
180
ISSN(印刷物)0933-033X

Fingerprint

Luminescence
Nanostructures
Spectroscopy
Photoluminescence
Cathodoluminescence
Excitons
Binding energy
Impurities
Inelastic scattering
Optical properties
Chemical activation
Doping (additives)
Temperature
LDS 751

All Science Journal Classification (ASJC) codes

  • Materials Science(all)

これを引用

Murotani, H., Yamada, Y., Nakamura, D., & Okada, T. (2014). Time and spatially resolved luminescence spectroscopy of ZnO nanostructures. : M. S. Ramachandra Rao, & T. Okada (版), ZnO Nanocrystals and Allied Materials (pp. 195-216). (Springer Series in Materials Science; 巻数 180). https://doi.org/10.1007/978-81-322-1160-0_9

Time and spatially resolved luminescence spectroscopy of ZnO nanostructures. / Murotani, Hideaki; Yamada, Yoichi; Nakamura, Daisuke; Okada, Tatsuo.

ZnO Nanocrystals and Allied Materials. 版 / M.S. Ramachandra Rao; Tatsuo Okada. 2014. p. 195-216 (Springer Series in Materials Science; 巻 180).

研究成果: 著書/レポートタイプへの貢献

Murotani, H, Yamada, Y, Nakamura, D & Okada, T 2014, Time and spatially resolved luminescence spectroscopy of ZnO nanostructures. : MS Ramachandra Rao & T Okada (版), ZnO Nanocrystals and Allied Materials. Springer Series in Materials Science, 巻. 180, pp. 195-216. https://doi.org/10.1007/978-81-322-1160-0_9
Murotani H, Yamada Y, Nakamura D, Okada T. Time and spatially resolved luminescence spectroscopy of ZnO nanostructures. : Ramachandra Rao MS, Okada T, 編集者, ZnO Nanocrystals and Allied Materials. 2014. p. 195-216. (Springer Series in Materials Science). https://doi.org/10.1007/978-81-322-1160-0_9
Murotani, Hideaki ; Yamada, Yoichi ; Nakamura, Daisuke ; Okada, Tatsuo. / Time and spatially resolved luminescence spectroscopy of ZnO nanostructures. ZnO Nanocrystals and Allied Materials. 編集者 / M.S. Ramachandra Rao ; Tatsuo Okada. 2014. pp. 195-216 (Springer Series in Materials Science).
@inbook{0caefba32d50475891ed918eb12e2c56,
title = "Time and spatially resolved luminescence spectroscopy of ZnO nanostructures",
abstract = "The optical properties of undoped, P-doped, and Sb-doped ZnO nanostructures (NSs) have been studied by means of photoluminescence (PL), time-resolved PL, and spatially resolved cathodoluminescence (CL) spectroscopy. The temperature dependence of the PL spectra of the P-doped and Sb-doped ZnO NSs was analyzed, and the binding energies of the P-acceptor- and the Sb-acceptor-bound excitons were estimated to be 15 and 11 meV, respectively. This indicated that the Sb impurities formed a shallower acceptor level than the P impurities in ZnO. PL lines due to the radiative recombination of biexcitons and the inelastic scattering processes of excitons were clearly observed in the undoped ZnO NSs, which enabled us to evaluate the binding energies of the excitons and biexcitons as 60 and 15 meV, respectively. These values were identical to the values in bulk ZnO. The radiative and nonradiative recombination lifetimes were estimated from the temperature dependence of the PL lifetime and the time-integrated PL intensity. Although the radiative recombination lifetimes for the undoped and P-doped ZnO NSs were almost equal, the nonradiative recombination lifetime for the P-doped ZnO NSs was longer than that for the undoped ZnO NSs. This suggested that the P doping suppressed the thermal activation of the nonradiative recombination processes. CL images revealed that the intensity of the side surface was much stronger than that of the interior in the P-doped ZnO NSs. On the other hand, the CL intensity was distributed almost uniformly in the Sb-doped.",
author = "Hideaki Murotani and Yoichi Yamada and Daisuke Nakamura and Tatsuo Okada",
year = "2014",
month = "1",
day = "1",
doi = "10.1007/978-81-322-1160-0_9",
language = "English",
isbn = "9788132211594",
series = "Springer Series in Materials Science",
pages = "195--216",
editor = "{Ramachandra Rao}, M.S. and Tatsuo Okada",
booktitle = "ZnO Nanocrystals and Allied Materials",

}

TY - CHAP

T1 - Time and spatially resolved luminescence spectroscopy of ZnO nanostructures

AU - Murotani, Hideaki

AU - Yamada, Yoichi

AU - Nakamura, Daisuke

AU - Okada, Tatsuo

PY - 2014/1/1

Y1 - 2014/1/1

N2 - The optical properties of undoped, P-doped, and Sb-doped ZnO nanostructures (NSs) have been studied by means of photoluminescence (PL), time-resolved PL, and spatially resolved cathodoluminescence (CL) spectroscopy. The temperature dependence of the PL spectra of the P-doped and Sb-doped ZnO NSs was analyzed, and the binding energies of the P-acceptor- and the Sb-acceptor-bound excitons were estimated to be 15 and 11 meV, respectively. This indicated that the Sb impurities formed a shallower acceptor level than the P impurities in ZnO. PL lines due to the radiative recombination of biexcitons and the inelastic scattering processes of excitons were clearly observed in the undoped ZnO NSs, which enabled us to evaluate the binding energies of the excitons and biexcitons as 60 and 15 meV, respectively. These values were identical to the values in bulk ZnO. The radiative and nonradiative recombination lifetimes were estimated from the temperature dependence of the PL lifetime and the time-integrated PL intensity. Although the radiative recombination lifetimes for the undoped and P-doped ZnO NSs were almost equal, the nonradiative recombination lifetime for the P-doped ZnO NSs was longer than that for the undoped ZnO NSs. This suggested that the P doping suppressed the thermal activation of the nonradiative recombination processes. CL images revealed that the intensity of the side surface was much stronger than that of the interior in the P-doped ZnO NSs. On the other hand, the CL intensity was distributed almost uniformly in the Sb-doped.

AB - The optical properties of undoped, P-doped, and Sb-doped ZnO nanostructures (NSs) have been studied by means of photoluminescence (PL), time-resolved PL, and spatially resolved cathodoluminescence (CL) spectroscopy. The temperature dependence of the PL spectra of the P-doped and Sb-doped ZnO NSs was analyzed, and the binding energies of the P-acceptor- and the Sb-acceptor-bound excitons were estimated to be 15 and 11 meV, respectively. This indicated that the Sb impurities formed a shallower acceptor level than the P impurities in ZnO. PL lines due to the radiative recombination of biexcitons and the inelastic scattering processes of excitons were clearly observed in the undoped ZnO NSs, which enabled us to evaluate the binding energies of the excitons and biexcitons as 60 and 15 meV, respectively. These values were identical to the values in bulk ZnO. The radiative and nonradiative recombination lifetimes were estimated from the temperature dependence of the PL lifetime and the time-integrated PL intensity. Although the radiative recombination lifetimes for the undoped and P-doped ZnO NSs were almost equal, the nonradiative recombination lifetime for the P-doped ZnO NSs was longer than that for the undoped ZnO NSs. This suggested that the P doping suppressed the thermal activation of the nonradiative recombination processes. CL images revealed that the intensity of the side surface was much stronger than that of the interior in the P-doped ZnO NSs. On the other hand, the CL intensity was distributed almost uniformly in the Sb-doped.

UR - http://www.scopus.com/inward/record.url?scp=84884242873&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84884242873&partnerID=8YFLogxK

U2 - 10.1007/978-81-322-1160-0_9

DO - 10.1007/978-81-322-1160-0_9

M3 - Chapter

SN - 9788132211594

T3 - Springer Series in Materials Science

SP - 195

EP - 216

BT - ZnO Nanocrystals and Allied Materials

A2 - Ramachandra Rao, M.S.

A2 - Okada, Tatsuo

ER -