Time dependence of nucleation density and crystallinity of diamond in low-pressure, ion-enhanced deposition

Y. Kouzuma, K. Teii, S. Mizobe, K. Uchino, K. Muraoka

研究成果: ジャーナルへの寄稿学術誌査読

5 被引用数 (Scopus)

抄録

The nucleation density and crystallinity of diamond prepared in an electron cyclotron resonance plasma by applying a negative substrate bias have been studied as a function of bias run time. The mean ion energy onto the substrate was set at approximately 30 and 50 eV by controlling the bias voltage. For short bias times of 10-60 min, the nucleation density increased with time and the highest nucleation density (107-108 cm-2) and crystallinity were obtained at 60 min of biasing. For long bias times of 60-150 min, the nucleation density decreased with time accompanied by deterioration of the crystallinity, presumably due to a reduction of the effective substrate bias voltage caused by the delamination of the deposited amorphous carbon film. The incubation period for nucleation was estimated between 10 and 30 min, which was interpreted as the time to produce the amorphous carbon hydrogenated matrix characterized by relatively ordered structures with respect to carbon sp2 phase.

本文言語英語
ページ(範囲)656-660
ページ数5
ジャーナルDiamond and Related Materials
13
4-8
DOI
出版ステータス出版済み - 4月 2004

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 化学 (全般)
  • 機械工学
  • 材料化学
  • 電子工学および電気工学

フィンガープリント

「Time dependence of nucleation density and crystallinity of diamond in low-pressure, ion-enhanced deposition」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル