Transmission electron microscopy analysis of nanorods in BaSnO 3 -doped ErBa 2 Cu 3 O 7-δ films

Kazuhiro Yamada, Ataru Ichinose, Shuhei Yasunaga, Ryo Teranishi, Masashi Mukaida, Shigeru Horii, Ryusuke Kita, Shingo Kato, Yutaka Yoshida, Kaname Matsumoto, Shoichi Toh

    研究成果: Contribution to journalArticle査読

    9 被引用数 (Scopus)

    抄録

    Microstructures of BaSnO 3 -doped ErBa 2 Cu 3 O 7_δ films were studied by transmission electron microscopy. BaSnO 3 -doped ErBa 2 Cu 3 O 7-δ films were grown by a pulsed laser deposition method. In the cross-sectional transmission electron microscopy observation, the presence of nanorods with 10nm average diameter was confirmed from bright-field images, and these nanorods in turn contained tin (Sn), as confirmed from the energy-dispersive X-ray spectroscopy spectra. The crystal structure of the nanorod was determined to be cubic perovskite from its selected area electron diffraction pattern. Using the selected area electron diffraction patterns, the lattice constant of the nanorods in the ErBa 2 Cu 3 O 7-δ film was measured to be 0.414 nm. This was in good agreement with the lattice constant of BaSnO 3 , 0.412nm. Furthermore, parallel Moiré fringes were observed in the bright-field images, and the relationships between the lattice planes and Moiré fringes were investigated. It was thus confirmed that BaSnO 3 was dispersed in the ErBa 2 Cu 3 O 7-δ as nanorods.

    本文言語英語
    ページ(範囲)899-903
    ページ数5
    ジャーナルJapanese Journal of Applied Physics
    47
    2 PART 1
    DOI
    出版ステータス出版済み - 2 15 2008

    All Science Journal Classification (ASJC) codes

    • 工学(全般)
    • 物理学および天文学(全般)

    フィンガープリント

    「Transmission electron microscopy analysis of nanorods in BaSnO <sub>3</sub> -doped ErBa <sub>2</sub> Cu <sub>3</sub> O <sub>7-δ</sub> films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル