Tribological properties of poly(methyl methacrylate) brushes prepared by surface-initiated atom transfer radical polymerization

Hiroki Sakata, Motoyasu Kobayashi, Hideyuki Otsuka, Atsushi Takahara

研究成果: ジャーナルへの寄稿評論記事

84 引用 (Scopus)

抄録

Surface-initiated living radical polymerization of methyl methacrylate (MMA) using copper/bipyridyl complex was carried out from silicon wafer immobilized with a 2-bromoisobutylate moiety, resulting in the assembly of polymer chains tethered by one end to a surface, a so-called "polymer brush". The thickness of the PMMA brush, which was estimated by ellipsometry and atomic force microscopy, increased linearly with the molecular weight of the chains, and was controlled by the free initiator concentration. The graft density of the PMMA brushes was estimated to be as high as 0.56chains/nm2. The frictional properties of the high density PMMA brush were characterized by sliding the stainless ball probe on its surface across a width of 20 mm at a rate of 90 mm/min under loading of 0.49 N in air at room temperature. The PMMA brush was found to have a lower frictional coefficient and much better wear resistance than the corresponding spin-coated PMMA film because of the anchoring of the chain ends in the brush. In addition, the friction coefficient of the polymer brush significantly decreased in response to soaking in acetone and toluene, and increased in response to immersion in hexane. The tribological properties depended on the solvent quality.

元の言語英語
ページ(範囲)767-775
ページ数9
ジャーナルPolymer Journal
37
発行部数10
DOI
出版物ステータス出版済み - 12 19 2005

Fingerprint

Atom transfer radical polymerization
Polymethyl Methacrylate
Brushes
Polymethyl methacrylates
Polymers
2,2'-Dipyridyl
Living polymerization
Methacrylates
Ellipsometry
Toluene
Hexanes
Free radical polymerization
Acetone
Hexane
Silicon wafers
Grafts
Wear resistance
Copper
Atomic force microscopy
Molecular weight

All Science Journal Classification (ASJC) codes

  • Polymers and Plastics
  • Materials Chemistry

これを引用

Tribological properties of poly(methyl methacrylate) brushes prepared by surface-initiated atom transfer radical polymerization. / Sakata, Hiroki; Kobayashi, Motoyasu; Otsuka, Hideyuki; Takahara, Atsushi.

:: Polymer Journal, 巻 37, 番号 10, 19.12.2005, p. 767-775.

研究成果: ジャーナルへの寄稿評論記事

@article{abe3db63ebee4cd18f063ca90c836ff9,
title = "Tribological properties of poly(methyl methacrylate) brushes prepared by surface-initiated atom transfer radical polymerization",
abstract = "Surface-initiated living radical polymerization of methyl methacrylate (MMA) using copper/bipyridyl complex was carried out from silicon wafer immobilized with a 2-bromoisobutylate moiety, resulting in the assembly of polymer chains tethered by one end to a surface, a so-called {"}polymer brush{"}. The thickness of the PMMA brush, which was estimated by ellipsometry and atomic force microscopy, increased linearly with the molecular weight of the chains, and was controlled by the free initiator concentration. The graft density of the PMMA brushes was estimated to be as high as 0.56chains/nm2. The frictional properties of the high density PMMA brush were characterized by sliding the stainless ball probe on its surface across a width of 20 mm at a rate of 90 mm/min under loading of 0.49 N in air at room temperature. The PMMA brush was found to have a lower frictional coefficient and much better wear resistance than the corresponding spin-coated PMMA film because of the anchoring of the chain ends in the brush. In addition, the friction coefficient of the polymer brush significantly decreased in response to soaking in acetone and toluene, and increased in response to immersion in hexane. The tribological properties depended on the solvent quality.",
author = "Hiroki Sakata and Motoyasu Kobayashi and Hideyuki Otsuka and Atsushi Takahara",
year = "2005",
month = "12",
day = "19",
doi = "10.1295/polymj.37.767",
language = "English",
volume = "37",
pages = "767--775",
journal = "Polymer Journal",
issn = "0032-3896",
publisher = "Nature Publishing Group",
number = "10",

}

TY - JOUR

T1 - Tribological properties of poly(methyl methacrylate) brushes prepared by surface-initiated atom transfer radical polymerization

AU - Sakata, Hiroki

AU - Kobayashi, Motoyasu

AU - Otsuka, Hideyuki

AU - Takahara, Atsushi

PY - 2005/12/19

Y1 - 2005/12/19

N2 - Surface-initiated living radical polymerization of methyl methacrylate (MMA) using copper/bipyridyl complex was carried out from silicon wafer immobilized with a 2-bromoisobutylate moiety, resulting in the assembly of polymer chains tethered by one end to a surface, a so-called "polymer brush". The thickness of the PMMA brush, which was estimated by ellipsometry and atomic force microscopy, increased linearly with the molecular weight of the chains, and was controlled by the free initiator concentration. The graft density of the PMMA brushes was estimated to be as high as 0.56chains/nm2. The frictional properties of the high density PMMA brush were characterized by sliding the stainless ball probe on its surface across a width of 20 mm at a rate of 90 mm/min under loading of 0.49 N in air at room temperature. The PMMA brush was found to have a lower frictional coefficient and much better wear resistance than the corresponding spin-coated PMMA film because of the anchoring of the chain ends in the brush. In addition, the friction coefficient of the polymer brush significantly decreased in response to soaking in acetone and toluene, and increased in response to immersion in hexane. The tribological properties depended on the solvent quality.

AB - Surface-initiated living radical polymerization of methyl methacrylate (MMA) using copper/bipyridyl complex was carried out from silicon wafer immobilized with a 2-bromoisobutylate moiety, resulting in the assembly of polymer chains tethered by one end to a surface, a so-called "polymer brush". The thickness of the PMMA brush, which was estimated by ellipsometry and atomic force microscopy, increased linearly with the molecular weight of the chains, and was controlled by the free initiator concentration. The graft density of the PMMA brushes was estimated to be as high as 0.56chains/nm2. The frictional properties of the high density PMMA brush were characterized by sliding the stainless ball probe on its surface across a width of 20 mm at a rate of 90 mm/min under loading of 0.49 N in air at room temperature. The PMMA brush was found to have a lower frictional coefficient and much better wear resistance than the corresponding spin-coated PMMA film because of the anchoring of the chain ends in the brush. In addition, the friction coefficient of the polymer brush significantly decreased in response to soaking in acetone and toluene, and increased in response to immersion in hexane. The tribological properties depended on the solvent quality.

UR - http://www.scopus.com/inward/record.url?scp=28844450331&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=28844450331&partnerID=8YFLogxK

U2 - 10.1295/polymj.37.767

DO - 10.1295/polymj.37.767

M3 - Review article

AN - SCOPUS:28844450331

VL - 37

SP - 767

EP - 775

JO - Polymer Journal

JF - Polymer Journal

SN - 0032-3896

IS - 10

ER -