Ultrasonic Fatigue Properties of a High Strength Extruded Al Alloy

Norio Kawagoishi, Qiang Chen, Nu Yan, Qingyuan Wang, Eiji Kondo

研究成果: ジャーナルへの寄稿記事

8 引用 (Scopus)

抄録

In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.

元の言語英語
ページ(範囲)1672-1677
ページ数6
ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
69
発行部数12
出版物ステータス出版済み - 12 1 2003
外部発表Yes

Fingerprint

Ultrasonics
Fatigue of materials
Crack propagation
High strength alloys
Bending (deformation)
Crack initiation
Cracks
Fatigue strength

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Ultrasonic Fatigue Properties of a High Strength Extruded Al Alloy. / Kawagoishi, Norio; Chen, Qiang; Yan, Nu; Wang, Qingyuan; Kondo, Eiji.

:: Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 巻 69, 番号 12, 01.12.2003, p. 1672-1677.

研究成果: ジャーナルへの寄稿記事

@article{c74902e5d86446ac9724209a621b92b8,
title = "Ultrasonic Fatigue Properties of a High Strength Extruded Al Alloy",
abstract = "In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.",
author = "Norio Kawagoishi and Qiang Chen and Nu Yan and Qingyuan Wang and Eiji Kondo",
year = "2003",
month = "12",
day = "1",
language = "English",
volume = "69",
pages = "1672--1677",
journal = "Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A",
issn = "0387-5008",
publisher = "一般社団法人日本機械学会",
number = "12",

}

TY - JOUR

T1 - Ultrasonic Fatigue Properties of a High Strength Extruded Al Alloy

AU - Kawagoishi, Norio

AU - Chen, Qiang

AU - Yan, Nu

AU - Wang, Qingyuan

AU - Kondo, Eiji

PY - 2003/12/1

Y1 - 2003/12/1

N2 - In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.

AB - In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.

UR - http://www.scopus.com/inward/record.url?scp=1442314736&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=1442314736&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:1442314736

VL - 69

SP - 1672

EP - 1677

JO - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

JF - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

SN - 0387-5008

IS - 12

ER -