Wettability and interaction between molten Al and Ni-coated Al2O3 or pure Ni substrate

Nobuyuki Mori, Hirofumi Miyahara, Masaaki Koga, Keisaku Ogi

    研究成果: Contribution to journalArticle査読

    6 被引用数 (Scopus)

    抄録

    The influence of Ni ion plating 0.1 to 3.1 μm thick on the wettability of molten Al to Al2O3 was measured by the sessile drop method in a vacuum of 2 × 10-3 Pa at temperatures from 973 to 1173 K. The wetting angle of molten Al to Al2O3 decreased from 110° to 90° as the temperature rose from 973 to 1173 K. Ni coating on Al2O3 reduced the wetting angle to less than 10° when the thickness of coating was larger than 0.1, 0.5, and 0.8 μm at 973, 1073 and 1173 K, respectively. The thinner Ni coating could not improve the wettability, because the Ni deposits on Al2O3 were coagulated by surface tension and pores were generated in Ni coating. The development of pores became more remarkable as temperature rose, making the molten Al which once spread on the Ni coating move back towards the receding wetting angle to Al2O3. The interaction between the coated Ni and the molten Al was also metallographically investigated.

    本文言語英語
    ページ(範囲)444-451
    ページ数8
    ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
    55
    4
    DOI
    出版ステータス出版済み - 1991

    All Science Journal Classification (ASJC) codes

    • 凝縮系物理学
    • 材料力学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Wettability and interaction between molten Al and Ni-coated Al<sub>2</sub>O<sub>3</sub> or pure Ni substrate」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル