Wettability and Interfacial Reaction between Molten lron and Zirconia Substrates

Kunihiko Nakashima, Kenji Takihira, Takashi Miyazaki, Katsumi Mori

    研究成果: Contribution to journalArticle査読

    12 被引用数 (Scopus)

    抄録

    The surface tension of, and the contact angle formed by, molten iron on three types of commercial zirconia substrates containing 8 mol% Y2O3, 9 mol% MgO, or 11 mol% CaO were measured over a wide range of oxygen concentration in the molten iron by the sessile drop method. The solidified metal–substrate interface was examined in an SEM equipped with an EPMA. The surface tension of molten iron decreased with increasing oxygen concentration. The contact angle of molten iron increased rapidly with increasing oxygen concentration and reached a local maximum value at an oxgyen concentration of ∼100 ppm, and then decreased with increasing oxygen concentration. At lower oxygen concentration, dissociation of ZrO2 was observed. For the ZrO2–9 mol% MgO substrate, segregation of MgO to the interface was observed. For the ZrO2–11 mol% CaO substrate, segregation of CaO and the precipitation of small ZrO2 particles in the segregation layer of CaO were observed at the interface. Conversely, at higher oxygen concentration, penetration of molten iron into the grain boundaries was observed in all types of zirconia substrates.

    本文言語英語
    ページ(範囲)3000-3008
    ページ数9
    ジャーナルJournal of the American Ceramic Society
    76
    12
    DOI
    出版ステータス出版済み - 12 1993

    All Science Journal Classification (ASJC) codes

    • セラミックおよび複合材料
    • 材料化学

    フィンガープリント

    「Wettability and Interfacial Reaction between Molten lron and Zirconia Substrates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル