Wettability of Al2O3 Substrate by Liquid Iron—Effects of Oxygen in Liquid Iron and Purity of Al2O3 Substrate—

Kunihiko Nakashima, Katsumi Mori, Kenji Takihira, Nobuya Shinozaki

    研究成果: Contribution to journalArticle査読

    36 被引用数 (Scopus)

    抄録

    The interfacial properties between liquid Fe-O alloy and alumina substrates with different purities, 99.9% and 96% Al2O3, were measured by the sessile drop method. The interfaces of samples were examined by SEM and EPMA after the experiment. It was found that the surface tension decreased with increasing oxygen concentration in the iron for both substrates. The contact angle of 99.9% Al2O3 abruptly increased with increasing oxygen concentration at lower oxygen concentrations. These phenomena were attributed to the dissociation of Al2O3. Moreover, at higher oxygen concentration, the formation of the dense hercynite was observed at the Fe-O/Al2O3 interface, the contact angle slightly decreased with increasing oxygen concentration. For 96% Al2O3, a Ca- or Mg-rich layer was observed at the interface at a lower oxygen concentration, the contact angle abruptly increased with increasing oxygen concentration. Whereas, at higher oxygen concentrations, the contact angle rapidly decreased with increasing oxygen concentration. Under these conditions, the formation of hercynite and the penetration of iron into the grain boundaries of Al2O3 substrates were observed.

    本文言語英語
    ページ(範囲)918-926
    ページ数9
    ジャーナルMaterials Transactions, JIM
    33
    10
    DOI
    出版ステータス出版済み - 1 1 1992

    All Science Journal Classification (ASJC) codes

    • 工学(全般)

    フィンガープリント

    「Wettability of Al<sub>2</sub>O<sub>3</sub> Substrate by Liquid Iron—Effects of Oxygen in Liquid Iron and Purity of Al<sub>2</sub>O<sub>3</sub> Substrate—」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル