TY - JOUR
T1 - Zinc phosphate coating on 316L-type stainless steel using hydrothermal treatment
AU - Valanezhad, A.
AU - Tsuru, Kanji
AU - Maruta, M.
AU - Kawachi, G.
AU - Matsuya, S.
AU - Ishikawa, Kunio
PY - 2010/12/25
Y1 - 2010/12/25
N2 - Parkerizing or zinc phosphatizing, a kind of zinc phosphate coating is utilized for mild steel to acquire a protective layer against a corrosion reaction. Although this method is useful for mild steels, it is not possible for 316L-type stainless steels (316L SS) because of their lower chemical reactivity. In order to investigate the possibility of preparing zinc phosphate coating on 316L SS, substrates were subjected to hydrothermal treatment in zinc phosphate solution at different temperatures and duration times. SEM observation with EDX analysis showed that the zinc phosphate coating layer was successfully prepared at 200°C for 24h. Besides, XRD results indicated that the crystal phase of the coating layer was assigned to zinclipscombite (ZnFe3+2(PO4)2(OH)2). Adhesive test indicated that the coating layer was strongly attached on the 316L SS substrate (more than 12.0±1.4MPa).
AB - Parkerizing or zinc phosphatizing, a kind of zinc phosphate coating is utilized for mild steel to acquire a protective layer against a corrosion reaction. Although this method is useful for mild steels, it is not possible for 316L-type stainless steels (316L SS) because of their lower chemical reactivity. In order to investigate the possibility of preparing zinc phosphate coating on 316L SS, substrates were subjected to hydrothermal treatment in zinc phosphate solution at different temperatures and duration times. SEM observation with EDX analysis showed that the zinc phosphate coating layer was successfully prepared at 200°C for 24h. Besides, XRD results indicated that the crystal phase of the coating layer was assigned to zinclipscombite (ZnFe3+2(PO4)2(OH)2). Adhesive test indicated that the coating layer was strongly attached on the 316L SS substrate (more than 12.0±1.4MPa).
UR - http://www.scopus.com/inward/record.url?scp=78649729358&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=78649729358&partnerID=8YFLogxK
U2 - 10.1016/j.surfcoat.2010.09.050
DO - 10.1016/j.surfcoat.2010.09.050
M3 - Article
AN - SCOPUS:78649729358
VL - 205
SP - 2538
EP - 2541
JO - Surface and Coatings Technology
JF - Surface and Coatings Technology
SN - 0257-8972
IS - 7
ER -